Daxun is an excellent manufacturer of CP Grade 4 titanium rods and bars.
- Titanium bar grade: UNS R50700
- Tipos de barras de titanio: barras laminadas, barras estiradas, barras de titanio forjado
- Principales normas: ASTM ASME GB GJB EN JIS DIN ISO ATP BS, etc.
- High corrosion resistance, excellent weldability, superior strength, lightweight, and outstanding performance in aggressive environments.
The global leader in commercially titanium alloy rod manufacturing services
Daxun, specializing in the production of alloy titanium rods for extreme environments
CP Grade 4 titanium bar represents the highest strength variant within the commercially pure titanium family, combining exceptional mechanical properties with outstanding corrosion resistance. As an unalloyed titanium grade, it maintains the inherent biocompatibility and weldability of pure titanium while delivering significantly enhanced tensile strength, with minimum yield strength reaching 480 MPa and ultimate tensile strength exceeding 550 MPa. This unique combination makes CP Grade 4 titanium bars particularly valuable in applications demanding both structural integrity and environmental durability.
The chemical composition of CP Grade 4 titanium bar consists primarily of titanium with controlled amounts of oxygen (0.40% maximum), iron (0.50% maximum), carbon (0.08% maximum), and nitrogen (0.05% maximum). The elevated oxygen content compared to other CP grades directly contributes to its superior strength characteristics. These bars exhibit excellent ductility, allowing for various forming processes while maintaining their enhanced mechanical properties, making them suitable for cold working, machining, and fabrication into complex components.
Key Application Areas
- Aerospace: Used for critical structural components, aircraft fasteners, and springs where high strength-to-weight ratio is essential.
- Procesamiento químico: Ideal for pump shafts, valve components, and heat exchanger parts exposed to aggressive media.
- Marine Engineering: Employed for hardware and components that require long-term durability in seawater.
- Medical Implants: Utilized for surgical instruments and implant devices that demand both high strength and biocompatibility.
Manufacturing & Product Forms
- Production Processes: Can be produced through hot rolling, forging, or extrusion, followed by annealing.
- Available Forms: Supplied in various shapes, including round, square, hexagonal, and flat bars.
- Custom Dimensions: Available in a wide range of sizes, with options for custom dimensions to meet specific project needs.
- Machining: Can be effectively machined using appropriate tooling and cooling strategies, though it requires more robust parameters than lower titanium grades.
| Especificación | Detalles |
|---|---|
| Material | CP Grade 4 Titanium Bar |
| Estándar | ASTM B348, ASTM F67, AMS 4921, ISO 5832-2 |
| Dimensiones | EN, ASTM, JIS, ASME, BS, AISI, GB, GJB, DIN |
| Diámetro | 0.125″ – 14″ (3.175mm – 355.6mm), custom |
| Longitud Alcance | Up to 240″ (6096mm), custom |
| Formulario | Round Bar, Square Bar, Hexagonal Bar |
| Acabado superficial | Cold drawn, Centerless Ground, Polished, Rough Turned, Black, NO.4 Finish, BA Finish, Matt Finish |
| Condición | Annealed, Hardened & tempered |
| Tolerancia | Diameter tolerance: +/- 0.005″ (0.127mm), length tolerance: +/- 0.125″ (3.175mm) |
| Formulario | Titanium square bars, titanium ingots, titanium round bars, rectangular titanium bars, triangular titanium bars, forged titanium bars, titanium hexagonal bars |
Datos
- Chemical Composition (% by Weight)
- Propiedades mecánicas
- Propiedades físicas
| Elemento | Minimum | Maximum |
|---|---|---|
| Titanium (Ti) | 99.2 | - |
| Oxygen (O) | 0.35 | 0.40 |
| Hierro (Fe) | - | 0.50 |
| Carbon © | - | 0.08 |
| Nitrogen (N) | - | 0.05 |
| Hydrogen (H) | - | 0.015 |
| Propiedad | Minimum Value | Unit |
|---|---|---|
| Ultimate Tensile Strength | 550 | MPa |
| Yield Strength (0.2% offset) | 480 | MPa |
| Elongation | 15 | % |
| Reducción de la superficie | 30 | % |
| Brinell Hardness | 320 | HBW |
| Modulus of Rigidity | 44 | GPa |
| Propiedad | Valor | Unit |
|---|---|---|
| Densidad | 4.51 | g/cm³ |
| Punto de fusión | 1668 | °C |
| Módulo de elasticidad | 105 | GPa |
| Conductividad térmica | 16.4 | W/m·K |
| Resistividad eléctrica | 560 | nΩ·m |
| Specific Heat | 0.52 | J/g·K |
Elija Daxun para que su proyecto despegue.
Ventajas de la fábrica de Daxun
El concepto de “Gestión de la Excelencia en el Rendimiento” de Daxun promueve el modelo de gestión “PDCA + Lean”. La tarjeta de visita de la empresa dice “Daxun = Calidad fiable”. Daxun utiliza el sistema ERP para lograr la trazabilidad completa de la variedad, especificación y origen de cada barra de titanio, y defiende y fomenta la lucha contra la falsificación en la industria. Daxun confía en la tecnología para el procesamiento y la personalización, y la alta precisión y la alta calidad son los puntos de referencia de la industria; en términos de servicio, promueve la gestión del ciclo de vida del producto, proporciona soluciones profesionales de selección de materiales y procesamiento antes de las ventas, supervisa estrictamente durante las ventas y proporciona garantías de servicio sin preocupaciones después de las ventas.
CP Grade 4 Titanium Rod Production Method
Daxun produce barras de titanio de alta calidad y alto rendimiento, y también puede fabricar según el acuerdo del cliente:
- Los lingotes de titanio deben someterse a tratamiento térmico y mecanizado, pruebas de ultrasonidos por inmersión, pruebas de propiedades mecánicas, inspección estructural macroscópica y microscópica y otros procesos. Proceso de producción: barras de titanio laminado en caliente - alta eficiencia, rendimiento estable, barras de titanio forjado - tamaño flexible, forja multi-fuego, mejorar el rendimiento integral de barras de titanio, barras de titanio estirado en frío - barras de titanio de alta precisión por lo general de pequeño tamaño; las barras de titanio anteriores se entregan con superficie brillante.
Calidad, entrega, inspección
Daxun performs several quality assurance tests, these tests include mechanical tests like area tensile, chemical analysis, material positive identification – PMI test, micro and macro testing, intergranular corrosion (IGC) test, ultrasonic flaw detection test, pitting and resistance test, hardness test, material positive identification, expansion test etc. All these tests ensure that the CP Grade 4 Titanium Rod and CP Grade 4 Titanium Round Bar material is suitable for the required application. During the production process, we measure the diameter, thickness and surface of the product.
- Nuestro plazo de entrega se ajusta estrictamente a lo estipulado en el contrato.
- Apoyar a las agencias externas del cliente para que vayan a la fábrica a inspeccionar
- Muestras gratuitas para las pruebas de los clientes
- Apoyo a la inspección in situ o por vídeo en fábrica
Embalaje
Daxun Alloy garantiza la mejor calidad de embalaje, ya que desempeña un papel importante en el transporte internacional de mercancías, donde las mercancías pasan por varios canales para llegar al destino final, por lo que prestamos especial atención al embalaje. Embalamos nuestras mercancías de muchas maneras dependiendo del producto. Embalamos nuestros productos de muchas maneras, tales como:
- Cajas y cajones
- Retráctil
- Palés de madera
- Cajas de madera
Asistencia técnica
Si necesita asistencia técnica adicional, nuestro metalúrgico residente y nuestro personal experto estarán encantados de ayudarle. Además, Daxun cuenta con un laboratorio de pruebas certificado, una primicia en la industria de inventarios multimetal y plástico. Esto, en nuestra opinión, demuestra nuestra inquebrantable dedicación a la calidad y nuestra filosofía como proveedor de servicios completos.
Daxun CP Grade 4 Titanium Rods help your brand improve quickly
- Tolerances for CP Grade 4 Titanium Round Bars
|
TAMAÑO NOMINAL
|
h5
|
h6
|
h7
|
h8
|
h9
|
H10
|
H11
|
h12
|
|
DIÁMETRO mm
|
||||||||
| ~ a 3 | +0.004/0 | +0.006/0 | +0.01/0 | +0.014/0 | +0.025/0 | +0.04/0 | +0.06/0 | +0.1/0 |
| de 3 a 6 años | +0.005/0 | +0.008/0 | +0.012/0 | +0.018/0 | +0.03/0 | +0.048/0 | +0.075/0 | +0.12/0 |
| de 6 a 10 años | +0.006/0 | +0.009/0 | +0.015/0 | +0.022/0 | +0.036/0 | +0.058/0 | +0.09/0 | +0.15/0 |
| de 10 a 18 años | +0.008/0 | +0.011/0 | +0.018/0 | +0.027/0 | +0.043/0 | +0.07/0 | +0.11/0 | +0.18/0 |
| de 18 a 30 años | +0.009/0 | +0.013/0 | +0.021/0 | +0.033/0 | +0.052/0 | +0.084/0 | +0.13/0 | +0.21/0 |
| más de 30 a 50 | +0.011/0 | +0.016/0 | +0.025/0 | +0.039/0 | +0.062/0 | +0.1/0 | +0.16/0 | +0.25/0 |
| más de 50 a 80 | +0.013/0 | +0.019/0 | +0.03/0 | +0.046/0 | +0.074/0 | +0.12/0 | +0.19/0 | +0.3/0 |
| más de 80 a 120 | +0.015/0 | +0.022/0 | +0.035/0 | +0.054/0 | +0.087/0 | +0.14/0 | +0.22/0 | +0.35/0 |
| más de 120 a 180 | +0.018/0 | +0.025/0 | +0.04/0 | +0.063/0 | +0.1/0 | +0.16/0 | +0.25/0 | +0.4/0 |
| más de 180 a 250 | +0.02/0 | +0.029/0 | +0.046/0 | +0.072/0 | +0.115/0 | +0.185/0 | +0.29/0 | +0.46/0 |
Varilla de titanio
Proyectos y productos recientes
Productos relacionados (6)
CP Grade 4 is the strongest of all the commercially pure titanium grades. Its key differentiator is its higher oxygen content, which gives it a minimum yield strength of 480 MPa, significantly higher than CP Grade 2 (275 MPa). This makes it the preferred choice when high strength and durability are critical, while still maintaining excellent corrosion resistance.
Due to its high strength-to-weight ratio and biocompatibility, CP Grade 4 titanium bar is widely used in the aerospace industry for fasteners and springs, in chemical processing for pump and valve components, in marine engineering for durable hardware, and in the medical field for surgical instruments and implants that require superior structural integrity.
While it is more challenging to machine than lower grades due to its strength, it can be effectively machined with proper tooling and cooling. It is also readily weldable using standard methods like TIG welding, but it requires an inert gas shield (like argon) to protect the weld area from atmospheric contamination and prevent embrittlement.
The primary advantage is its superior corrosion resistance, especially in chloride environments like seawater, where stainless steel is prone to pitting and stress corrosion cracking. CP Grade 4 also offers a much better strength-to-weight ratio. Although the initial cost is higher, its extended service life and reduced maintenance in harsh environments often result in a lower total cost of ownership.
Rellene el formulario de la página “Contacto” o llame a nuestro responsable de ventas al “+86 13382898899”, nos pondremos en contacto con usted lo antes posible. Nuestro WhatsApp está en línea, y el correo electrónico ([email protected]) se comprobará en un plazo de 6 horas. Cada consulta o mensaje será respondido con prontitud. Además, compartimos información de mercado con nuestros clientes cada semana
Podemos proporcionarle muestras de barras de titanio para que compruebe la calidad. La muestra es gratis y usted sólo paga el flete.
Hemos exportado a más de 42 países, como Canadá, Chile, Kuwait, Alemania, Corea del Sur, Arabia Saudí, Singapur, etc.
Los pedidos de prueba pueden entregarse en una semana. Los pedidos normales tardan unas dos semanas.