Daxun has a state-of-the-art production facility in China that produces highly competitive, high-precision Grade 5 titanium bars. Excellent surface, tolerance, straightness and material quality provide you with technological leadership and consistent production processes. These advantages apply to a wide range of diameters and materials. In addition, our comprehensive stock program at our service center enables just-in-time delivery.

사양

AMS 4928 – Bars, Forgings, and Forging Stock (Annealed)

AMS 4965 – Bars, Forgings (Solution treated and aged)

AMS 4967 – Bars, Forgings (Annealed, Heat Treatable)

열 치료

• When high hardness, tensile strength, and fatigue strength are required, annealing can be performed at 1,700-1,900°F (927 – 1,038°C).
  DAXUN 6-4™ Grade 5 alloy can be heat treated in a variety of ways.
• 1. Anneal: 1,275 -1,400°F; (691 – 760°C), ½ to 2 hours, air or furnace cool
• 2. Stress Relief Anneal: 1,000 -1,200°F; (538 – 649°C), 1 to 8 hours, air or furnace cool
• 3. Solution Heat Treat: 1,675 -1,750°F; (913 – 954°C), 1 hour, water quench
• 4. Aging: 975 -1,025°F; (524 – 552°C), 4 to 8 hours – air cool

In the solution treated and aged condition, rapid quenching of small sections yields optimum properties. Larger section sizes and/or delayed quenching may result in less than optimum properties.

경도

Typical hardness in the annealed condition is Rockwell C 30-34, and about Rockwell C 35-39 in the solution and aged condition.

Forgeability/Formability

• Ti-6Al-4V, Grade 5 alloy bar is forged at 1,750°F; (954°C) with a final forging temperature of 1,450°F; (788°C). A minimum of 35% reduction is recommended for optimum properties.
• Ti-6Al-4V, Grade 5 alloy bar is difficult to form at room temperature, even in the annealed condition. Therefore, severe forming operations such as bending or stretching can be performed on annealed material at temperatures up to 1,200°F; (649°C) without affecting mechanical properties. Hot sizing or forming can be accomplished by creep forming in the range of 1,000 – 1,200°F; (538 – 649°C).

기계 가공성

Ti-6Al-4V, Grade 5 alloy bar can be machined using austenitic stainless steel machining methods with slow machining speeds, high feeds, rigid tools, and the use of large amounts of non-chlorinated cutting fluids.

용접성

Ti-6Al-4V, Grade 5 alloy rod is readily weldable in the annealed condition or in the solution and partially aged condition, with aging being accomplished during post weld heat treatment. Precautions must be taken to prevent contamination with oxygen, nitrogen, and hydrogen. Fusion welding may be performed in an inert gas filled chamber or with inert gas to weld the molten metal and adjacent heated zones, with a tail shield. Spot, seam, and flash welding may be performed without the aid of a protective atmosphere.

Special Considerations

Ti-6Al-4V, Grade 5 titanium alloy rod may be contaminated with hydrogen from improper pickling, and with oxygen, nitrogen, and carbon during forging, heat treating, brazing, etc. This contamination may result in a loss of ductility, which may adversely affect notch sensitivity and forming characteristics.

Size range

• Grade 1 Titanium Bar Dimensions
• Ø 0,7 – 30 mm (drawn, ground)
• Ø 16 – 400 mm (hot rolled, peeled)
• h11-h5 possible
• Tighter or different tolerances available on request
• Lengths up to 9,000 mm long, depending on diameter
• For larger diameters, other bar lengths and tolerances can be agreed upon request

Availability Grade 5 Titanium rods

• Drawing, straightening
• Drawing, straightening, polishing
• Drawing, grinding, polishing
• 그리기, 곧게 펴기, 연마, 연마하기
• Drawing, annealing, straightening
• Drawing, annealing, polishing
• Drawing, annealing, grinding, polishing
• Drawing, annealing, straightening, grinding, polishing

Processing

We produce bars according to your requirements.

Excellent surface and straightness, perfect roundness and tightest diameter tolerances (according to ISO 286-2 up to h5). Available in straightened, ground, polished conditions.

톱질

Band saws (up to Ø510 mm)
Bench band saws (up to 6,000 x 3,000 x 400 mm)
High-performance sawing machines for precise sawing

Titanium Bar end machining

Single or double sided
Chamfer 90° (45°)
Point 60° (30°)
Flat end
Centered

Delivery form

ASTM American Society for Testing and Materials Standards
AMS American Aerospace Materials Standards
NACE American Association of Corrosion Engineers International Standards
ASME American Society of Mechanical Engineers Standards
GB Chinese National Standards
GJB Chinese National Military Standards
ISO International Standards
DIN German Standards
EN European Standards
API American Petroleum Institute Standards

Detection method

Non-destructive testing > 100% testing

Testing methods
Eddy current testing/eddy current crack testing
Defect-free surface (level 4)
Flat bottom hole diameter 0.7 mm and 0.4 mm
Blind area can be cut off according to fixed length >Test to the end of the bar
Full diameter ultrasonic testing

Our Titanium Bar Material Services

• As an experienced service center, we can tailor your titanium bar material to your specifications, work with various certification bodies such as TÜV Rheinland or DNV to approve the specifications, and initiate the upgrading of titanium semi-finished products to meet appropriate applications.
• We will be happy to provide you with a consultation and explain everything you need to know about obtaining titanium bar material, including which standards require greater attention for the components to be manufactured.
• If you have a long-term supply commitment, you can establish a framework agreement with Daxun. We guarantee prices and quantities for a specified period.
• Benefit from our extensive experience in the global market. We have been helping businesses around the world since 2003. If you need any additional information about Grade 2 Titanium Bar, our professionals will be happy to help you. We look forward to hearing from you.

주문 정보

구매 주문서에는 수량, 등급, 유형 또는 카테고리, API5L 기준, 두께, 너비, 길이 및 화학 성분, 기계적 특성, 열처리, 추가 테스트, 제조 공정, 표면 코팅 또는 최종 마감과 관련된 모든 해당 부착물 또는 추가 요구 사항이 포함되어야 합니다. 지금 Daxun에 문의하시면 최대한 빨리 답변해 드리겠습니다.